3003 Anodized H 111 H 116 H 14 H 24 H 32 Aluminium Alloy Sheet For Liquid Containers
Product Description
After anodizing, the surface of the aluminum can produce a few microns-hundreds of microns of oxide film. Compared with the natural oxide film of aluminum alloy, its corrosion resistance, wear resistance and decorative properties have been significantly improved and improved. In fact, the direct current sulfuric acid anodic oxidation method is the most common application, because it is suitable for aluminum and most Anodizing of aluminum alloy; thicker film, hard and wear-resistant, better corrosion resistance after sealing; film colorless and transparent, strong adsorption capacity, easy to color; lower processing voltage, less power consumption ; The treatment process does not need to change the voltage cycle, which is conducive to continuous production and practical operation automation
3003 aluminum alloy is AL-Mn series alloy, which is the most widely used rust-proof aluminum. The strength of this alloy is not high (slightly higher than that of industrial pure aluminum) and cannot be strengthened by heat treatment. Therefore, cold working method is used to improve its mechanics Performance: It has a high plasticity in the annealed state, the plasticity is still good in the semi-cold work hardening, the plasticity is low in the cold work hardening, good corrosion resistance, and good weldability. Mainly used for low load parts that require high plasticity and good weldability, working in liquid or gaseous media, such as fuel tanks, gasoline or lubricant pipes, various liquid containers, and other small load parts made of deep drawing, wire Used to make rivets.
Chemical Composition
| |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
Mechanical properties:
| Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
| Min | |||||
| 3003 | O H111 | >0. 20—0. 50 | 95-135 | 35 | 15 |
| >0. 50 — 1. 50 | 17 | ||||
| >1. 50 — 3. 00 | 20 | ||||
| >3.00 — 6. 00 | 23 | ||||
| >6.0-12.5 | 24 | ||||
| >12.5-50 | |||||
| H12 | >0. 20—0. 50 | 120-160 | 90 | 3 | |
| >0. 50 — 1. 50 | 4 | ||||
| >1.50 — 3.00 | 5 | ||||
| >3. 00 — 6. 00 | 6 | ||||
| H14 | >0. 20 — 0. 50 | 145-195 | 125 | 2 | |
| >0. 5- 50 | 2 | ||||
| >1. 50 — 3. 00 | 3 | ||||
| >3. 00—6.0 | 4 | ||||
| H16 | >0. 20 — 0. 50 | 170-210 | 140 | 2 | |
| >0.50 — 1.50 | 3 | ||||
| >1. 50—4. 00 | 3 | ||||
| H18 | >0. 20 — 0. 50 | 190 | 170 | 1 | |
| >0. 50—1. 50 | 2 | ||||
| >1. 50 — 3. 00 | 2 | ||||
| H22 | >0. 20—0. 50 | 120-160 | 80 | 6 | |
| >0. 50 — 1.50 | 7 | ||||
| >1.50 — 3.00 | 8 | ||||
| >3. 0—6.0 | 9 | ||||
| H24 | >0. 20—0. 50 | 145-195 | 115 | 4 | |
| >0. 50 — 1.50 | 4 | ||||
| >1.50 —3. 00 | 5 | ||||
| H26 | >0. 20 — 0. 50 | 170-210 | 140 | 2 | |
| >0.50—1.50 | 3 | ||||
| >1.50 — 3. 00 | 3 | ||||
| H28 | >0,20 — 0,50 | 190 | 160 | 2 | |
| >0. 50〜L 50 | 2 | ||||
| >1. 50—3. 00 | 3 | ||||
| Aluminium Material Grade |
| 1)1000series aluminium /Pure Aluminum/Pure Aluminium:1050,1060,1070,1080,1100,1350,etc |
| 2)2000series aluminium alloy/Hard Aluminum/Hard Aluminium/Aluminum-Copper Alloy/ Aluminium-Copper Alloy:2011,2014,2017,2024,etc |
| 3)3000series aluminium alloy/ Rust-Proof Aluminum/Rust-Proof Aluminium/ Aluminum-Manganese Alloy:3002,3003,3104,3204,3030,etc |
| 4)5000series aluminium alloy/ Rust-Proof Aluminum/Rust-Proof Aluminium /Aluminum-Magnesium Alloy:5005,5025,5052,5040,5054,5056,5083,5152,etc |
| 5)6000series aluminium alloy / Aluminum-Magnesium-Silicon Alloy /Aluminium-Magnesium-Silicon Alloy /:6101,6003,6061,6063,6020,6201,6262,6082,etc |
| 6)7000series aluminium alloy/ Aluminum-Zinc Alloy/ Aluminium-Zinc Alloy:7003,7005,7050,7075,etc |
| 7)8000series aluminium alloy:8011,etc |
Product Photo
Company Introduction
| Equipment Production Parameters By Chongqing Dongchong Aluminum Co.,Ltd | |||||||
| 1650mm Slitting machine | Uncoil(MM) | Finished size(MM) | Slitting Width(MM) | ||||
| ID | OD | Width | Thickness | ID | OD | Above 0.5mm≥ 20mm | |
| Φ 400 | ≤ 1800 | ≤ 1600 | 0.5-4.5 | Φ 400 | ≤ 1700(normal) | ||
| Φ 500 | Φ500(normal) | ||||||
| Φ 600 | |||||||
| Aluminum foil Slitting machine | Uncoil(mm) | Finished size(MM) | |||||
| ID | OD | Width | Thickness | ID | OD | Width | |
| Φ 76 | ≤ 550 | ≤ 1200 | 0.08-0.12 | Φ76Φ76 | ≤ 550(normal) | ||
| 1450mm Crosscutting machine | Uncoil(MM) | Finished size(MM) | |||||
| ID | OD | Width | Thickness | ID | OD | Width | |
| Φ 505 | ≤ 1780 | ≤ 600 | 0.1-1.5 | Φ150 Φ500 | ≤ 1700(normal) | 6-600 | |
| Φ 605 | |||||||
| Annealling Furnace | Furnace Temperature | Furnace Size | |||||
| ≤440°C | 3200*2000*2100 | ||||||
| Saw Cutting | Thickness(mm) | Width (mm) | Length (mm) | ||||
|