Gold Anodized 5052 H 32 1.5 mm 2 mm 6 mm Aluminium Alloy Sheet For Decoration
Product Description
According to different surface treatment methods, aluminum alloy coil can be divided into Mirror surface aluminum plate, Brushed aluminum plate, Anodized aluminum plate, PE coated aluminum plate, PVDF coated aluminum plate etc.
After anodizing, the surface of the aluminum can produce a few microns-hundreds of microns of oxide film. Compared with the natural oxide film of aluminum alloy, its corrosion resistance, wear resistance and decorative properties have been significantly improved and improved. In fact, the direct current sulfuric acid anodic oxidation method is the most common application, because it is suitable for aluminum and most Anodizing of aluminum alloy; thicker film, hard and wear-resistant, better corrosion resistance after sealing; film colorless and transparent, strong adsorption capacity, easy to color; lower processing voltage, less power consumption ; The treatment process does not need to change the voltage cycle, which is conducive to continuous production and practical operation automation
Chemical Composition
| |||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| Aluminium Material Grade |
| 1)1000series aluminium /Pure Aluminum/Pure Aluminium:1050,1060,1070,1080,1100,1350,etc |
| 2)2000series aluminium alloy/Hard Aluminum/Hard Aluminium/Aluminum-Copper Alloy/ Aluminium-Copper Alloy:2011,2014,2017,2024,etc |
| 3)3000series aluminium alloy/ Rust-Proof Aluminum/Rust-Proof Aluminium/ Aluminum-Manganese Alloy:3002,3003,3104,3204,3030,etc |
| 4)5000series aluminium alloy/ Rust-Proof Aluminum/Rust-Proof Aluminium /Aluminum-Magnesium Alloy:5005,5025,5052,5040,5054,5056,5083,5152,etc |
| 5)6000series aluminium alloy / Aluminum-Magnesium-Silicon Alloy /Aluminium-Magnesium-Silicon Alloy /:6101,6003,6061,6063,6020,6201,6262,6082,etc |
| 6)7000series aluminium alloy/ Aluminum-Zinc Alloy/ Aluminium-Zinc Alloy:7003,7005,7050,7075,etc |
| 7)8000series aluminium alloy:8011,etc |
Mechanical properties:
| Alloy | Temper | Thickness(mm) | Tensile strength(Mpa) | Yeild strength(Mpa) | Elongation(%) |
| Min | |||||
| 5052 | H111 O | >0. 20 — 0. 50 | 170 — 215 | 65 | 12 |
| >0. 50 — 1. 50 | 14 | ||||
| >1.55 — 3.00 | 16 | ||||
| >3. 00 — 6. 00 | 18 | ||||
| >6.00 — 12. 50 | 165-215 | 19 | |||
| >12. 50 — 50.00 | — | ||||
| H12 | >0. 20 — 0. 50 | 210 — 260 | 160 | 4 | |
| >0.5-1.5 | 5 | ||||
| >1.50 —3.00 | 6 | ||||
| >3, 00 — 6. 00 | 8 | ||||
| H14 | >0. 20 — 0. 50 | 230-280 | 180 | 3 | |
| >0.50-1.50 | 3 | ||||
| >1. 50 -3. 00 | 4 | ||||
| >3.00 — 6.00 | 4 | ||||
| H16 | >0. 20 — 0, 50 | 250—300 | 210 | 2 | |
| >0. 50 — 1. 50 | 3 | ||||
| >1. 5- 3.0 | 3 | ||||
| >3.00 — 4. 00 | 3 | ||||
| H18 | >0. 20-0.50 | 270 | 240 | 1 | |
| >0. 50 — 1. 50 | 2 | ||||
| > 1.50 — 3.00 | 2 | ||||
| H22 H32 | >0. 20—0. 50 | 210 — 260 | 130 | 5 | |
| >0. 50-1.50 | 6 | ||||
| >1.50 — 3.00 | 7 | ||||
| >3. 00 — 6. 00 | 10 | ||||
| H24 H34 | >0. 20 — 0. 50 | 230 — 280 | 150 | 4 | |
| >0.50 — 1. 50 | 5 | ||||
| >1,50 — 3.00 | 6 | ||||
| >3.00 — 6.00 | 7 | ||||
| H26 H36 | >0. 20 — 0.50 | 250 — 300 | 180 | 3 | |
| >0. 50 — 1, 50 | 4 | ||||
| >1.50—3.00 | 5 | ||||
| >3. 00—4. 00 | 6 | ||||
| H38 H28 | >0. 20 — 0, 50 | 270 | 210 | 3 | |
| >0. 50~1. 5 | 3 | ||||
| >1. 50 — 3. 00 | 4 | ||||
| H112 | >6.00—12. 50 | 190 | 80 | 7 | |
| >12. 50 — 40,00 | 170 | 70 | |||
| >40, 00 — 80, 00 | 170 | 70 | |||
Product Photo
Company Introduction
| Equipment Production Parameters By Chongqing Dongchong Aluminum Co.,Ltd | |||||||
| 1650mm Slitting machine | Uncoil(MM) | Finished size(MM) | Slitting Width(MM) | ||||
| ID | OD | Width | Thickness | ID | OD | Above 0.5mm≥ 20mm | |
| Φ 400 | ≤ 1800 | ≤ 1600 | 0.5-4.5 | Φ 400 | ≤ 1700(normal) | ||
| Φ 500 | Φ500(normal) | ||||||
| Φ 600 | |||||||
| Aluminum foil Slitting machine | Uncoil(mm) | Finished size(MM) | |||||
| ID | OD | Width | Thickness | ID | OD | Width | |
| Φ 76 | ≤ 550 | ≤ 1200 | 0.08-0.12 | Φ76Φ76 | ≤ 550(normal) | ||
| 1450mm Crosscutting machine | Uncoil(MM) | Finished size(MM) | |||||
| ID | OD | Width | Thickness | ID | OD | Width | |
| Φ 505 | ≤ 1780 | ≤ 600 | 0.1-1.5 | Φ150 Φ500 | ≤ 1700(normal) | 6-600 | |
| Φ 605 | |||||||
| Annealling Furnace | Furnace Temperature | Furnace Size | |||||
| ≤440°C | 3200*2000*2100 | ||||||
| Saw Cutting | Thickness(mm) | Width (mm) | Length (mm) | ||||
| Size | Size | Tolerance | Size | ||||
| ≤200 | ≤2000 | ±0.3 | ≤3000 | ||||
|